Product Description

C12000 Phosphorus Deoxidized

Spec Equivalents: Low Residual P (DLP)

The C12000 - Phosphorus – Deoxidized copper is high on thermal and electrical conductivity. These alloys can freely be formed using copper and possess 95% IACS conductivity, low residual phosphorus, and high embrittlement resistance. The alloy is available in the form of rod, tube, and wire.

Specifications:

ASME SB111

ASTM B152

ASTM B359

ASTM B506

ASTM B716

ASME SB133

ASTM B187

ASTM B372

ASTM B623

ASTM B743

ASME SB359

ASTM B188

ASTM B395

ASTM B638

ASTM B75

ASME SB395

ASTM B224

ASTM B42

ASTM B640

ASTM B88

ASME SB42

ASTM B272

ASTM B442

ASTM B641

MIL B-18907

ASME SB75

ASTM B280

ASTM B447

ASTM B68

MIL B-20292

ASTM B111

ASTM B302

ASTM B451

ASTM B687

MIL T-24107

ASTM B133

ASTM B306

ASTM B5

ASTM B698

MIL T-3235

Chemical Composition:


Cu

Zn

Min/Max

99.9

0.5

Physical Properties:

  Properties

US Customary

Metric

Density

8.89 g/cm3

0.321 lb/in3

Melting point

1083°C

1981°F

Tensile strength, ultimate

221 - 393 MPa

32100 - 57000 psi

Tensile strength, yield (depending on temper)

69.0 - 365 MPa

10000 - 52900 psi

Elongation at break ( in 101.6 mm (4 in.))

55.00%

55.00%

Machinability (UNS C36000 (free-cutting brass) = 100%)

20.00%

20.00%

Poisson's ratio

0.34

0.34

Elastic modulus

117 GPa

16970 ksi

Sizes Available:

HOLLOW RODS

Min Bore Size 20 mm and Max OD 100 mm

ROUND RODS

8mm To 100 mm

HEX

10mm To 60mm

SQUARE

10mm To 60mm

FLAT

10mm Min Thickness and max Width 120mm

BILLETS

Up to 200 mm

INGOTS

As per Specification