Home » Products » Other Copper » C12000 - PHOSPHORUS - DEOXIDIZED, LOW RESIDUAL P

C12000 - PHOSPHORUS - DEOXIDIZED, LOW RESIDUAL P

C12000 - PHOSPHORUS - DEOXIDIZED, LOW RESIDUAL P
C12000 - PHOSPHORUS - DEOXIDIZED, LOW RESIDUAL P
Product Code : C12000
Product Description
C12000 Phosphorus Deoxidized













Spec Equivalents: Low Residual P (DLP)

The C12000 - Phosphorus – Deoxidized copper is high on thermal and electrical conductivity. These alloys can freely be formed using copper and possess 95% IACS conductivity, low residual phosphorus, and high embrittlement resistance. The alloy is available in the form of rod, tube, and wire.

Specifications:


ASME SB111 ASTM B152 ASTM B359 ASTM B506 ASTM B716


ASME SB133 ASTM B187 ASTM B372 ASTM B623 ASTM B743


ASME SB359 ASTM B188 ASTM B395 ASTM B638 ASTM B75


ASME SB395 ASTM B224 ASTM B42 ASTM B640 ASTM B88


ASME SB42 ASTM B272 ASTM B442 ASTM B641 MIL B-18907


ASME SB75 ASTM B280 ASTM B447 ASTM B68 MIL B-20292


ASTM B111 ASTM B302 ASTM B451 ASTM B687 MIL T-24107


ASTM B133 ASTM B306 ASTM B5 ASTM B698 MIL T-3235



Chemical Composition:
  Cu Zn
Min/Max 99.9 0.5

Physical Properties:
  Properties US Customary Metric
Density 8.89 g/cm3 0.321 lb/in3
Melting point 1083°C 1981°F
Tensile strength, ultimate 221 - 393 MPa 32100 - 57000 psi
Tensile strength, yield (depending on temper) 69.0 - 365 MPa 10000 - 52900 psi
Elongation at break ( in 101.6 mm (4 in.)) 55.00% 55.00%
Machinability (UNS C36000 (free-cutting brass) = 100%) 20.00% 20.00%
Poisson's ratio 0.34 0.34
Elastic modulus 117 GPa 16970 ksi

Sizes Available:
HOLLOW RODS Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS 8mm To 100 mm
HEX 10mm To 60mm
SQUARE 10mm To 60mm
FLAT 10mm Min Thickness and max Width 120mm
BILLETS Up to 200 mm
INGOTS As per Specification

Shree Extrusions Limited

Contact Us

( *represents compulsory fields )

Tips on getting accurate quotes. Please include product name, order quantity, usage, special requests if any in your inquiry.



SHREE EXTRUSIONS LTD. All Rights Reserved.