C37700 Forging Brass

480 INR/Kilograms

Get a Price/Quote

Product Details:

Click to View more

Request to Call Back Send Inquiry

Product Details
Product Description

C37700 Forging Brass Price And Quantity

Minimum Order Quantity 250 Kilograms
Price 480 INR/Kilograms
Price Range 450.00 - 500.00 INR/Kilograms

C37700 Forging Brass Trade Information

Supply Ability 20000 Kilograms Per Month
Delivery Time 4 Week

Product Description

We are providing c37700 forging brass in billets, ingots and sections form as per client requirement. The excellent hot working characteristic make this alloy ideal for forging to produce complex components. This alloy is good for both soldering and brazing. It is widely used to produce valve bodies for scuba, propane spray tank and agriculture spray tank. It possesses excellent machining characteristic for producing hardware, fitting and electrical components. This alloy holds high ductility, high thermal conductivity, excellent joining and plating characteristic. It also possesses non-magnetic property which not creates any spark in electrical fuse bodies. The offered c37700 forging brass is good for pressing of all kinds.

Features:

Corrosion resistance
Excellent surface finish
High tensile strength
Durability

C37700 Forging Bra

ASTM B124

The exceptional hot working characteristics of C37700 makes it the classic alloy for forgings. With outstanding flow characteristics, this alloy can be forged and machined into sophisticated and most complex components. C37700 can also easily be electroplated with various finish

Typical Uses for C37700 Forging Brass :-

Builders Hardware :Door Handles, Decorative Knobs, Furniture Hardware
Consumer :Golf Putters, Valve Bodies for Scuba & Propane Spray Tanks, Valve Bodies for Agricultural Spray Tanks
Electrical:Covers, Fuse Bodies
Industrial:Valve Components, Forgings and Pressings of All Kinds

Sizes Available:
HOLLOW RODS	Min Bore Size 20 mm and Max OD 100 mm
Round Rods	6mm To 130 mm
Hex	5mm To 60mm
Square	4mm To 60mm
FLAT	5mm Min Thickness and max Width 120mm
Profiles / Sections	AS per Customer Drawing
Billets	Up to 200 mm
Ingots	AS per Specification

Specifications:
Equivelent Specifications	Designation
Bar, Forging	ASTM B124
Forgings, Die	AMS 4614, ASME SB283, ASTM B283, SAE J461, J4623
Rod, Forging	AMS 4614, ASTM B124
Shapes, Forging	ASTM B124

Chemical Composition:
	Cu	Fe	Pb	Zn
Min/Max	58.0 - 61.0	0.3	1.5 - 2.5	Rem
Nominals	59.5	-	2	38

Specifications:
End Product	Designation
ISO	CuZn40Pb2
Europen	CuZn40Pb2
BS	CZ-122
JIS	C 3561
Russian	LS59-3

Fabrication:
Brazing	Suitability
Butt Weld	Fair
Capacity for Being Cold Worked	Poor
Capacity for Being Hot Formed	Excellent
Coated Metal Arc Welding	Not Recommended
Forgeability Rating	100
Gas Sheilded Arc Welding	Not Recommended
Machinability rating	80
Oxyacetylene Welding	Not Recommended
Seam Weld	Not Recommended
Soldering	Excellent
Spot Weld	Not Recommended

Physical Properties:
Product Property	US Customary	Metric
Coefficient of Thermal Expansion	11.5 ·10-6 per oF (68-572 F)	20.7 · 10 6? per °C (20-300 C)
Density	0.305 lb/in3 @ 68 F	8.44 gm/cm3 @ 20 C
Electrical Conductivity	27 %IACS @ 68 F	0.158 MegaSiemens/cm @ 20 C
Electrical Resistivity	38.4 ohms-cmil/ft @ 68 F	6.38 microhm-cm @ 20 C
Melting Point Liquid US	1640 F	893 C
Melting Point Solid US	1620 F	882 C
Modulas of Elasticity in Tension	15000 ksi	103400 MPa
Modulas of Rigidity	5600 ksi	38610 MPa
Specific Gravity	8.44	8.44
Specific Heat Capacity	0.09 Btu/lb/°F @ 68 F	377.1 J/kg · °K at 293 K
Thermal Conductivity	69.0 Btu ft/(hr · ft2 °F) @ 68 F	119.4 W/m · °K at 20 C