Backed with experienced team of technocrats, we manufacture, export and supply a wide gamut of C65100 Low Silicon Bronze. The provided product is widely used in various industries for manufacturing variety of components. The offered product is manufactured by our trained team of professionals using utmost quality metal alloys, this product is also tested on set quality parameters to enhanced their flawlessness. Available in various specifications to meet the wide requirements of clients, this C65100 Low Silicon Bronze is made available at competitive rates.
Features:
Robustly constructed
High strength
Dimensional accuracy
Corrosion resistance
Equivelent Specifications: | |
Specifications | Designation |
ISO | CuSi1 |
European | CuSi1 |
Czech Republic | CuSi1 |
Chemical Composition: | ||||||
| Cu | Fe | Pb | Mn | Si | Zn |
Min/Max | Rem | 0.8 | 0.05 | 0.7 | 0.80 - 2.0 | 1.5 |
Nominals | 98.5 | - | - | - | 1.5 | - |
Specifications: | |
End Product | Specification |
Bar | ASME SB98, ASTM B98 |
Bolts | ASTM F468 |
Nuts | ASTM F467 |
Pipe | ASTM B315 |
Plate | ASTM B96 |
Plate, Clad | ASTM B432 |
Rod | ASME SB98, ASTM B98 |
Screws | ASTM F468 |
Shapes | ASME SB98, ASTM B98 |
Sheet | ASTM B96 |
Strip | ASTM B96 |
Studs | ASTM F468 |
Tube | ASTM B315 |
Wire | ASTM B99, B105 |
Fabrication: | |
Joining Technique | Suitability |
Brazing | Excellent |
Butt Weld | Excellent |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Excellent |
Coated Metal Arc Welding | Fair |
Gas Shielded Arc Welding | Excellent |
Machinability Rating | 30 |
Oxyacetylene Welding | Good |
Seam Weld | Good |
Soldering | Excellent |
Spot Weld | Excellent |
Physical Properties: | ||
Product Property | US Customary | Metric |
Coefficient of Thermal Expansion | 9.9 ·10-6 per oF (68-212 F) | 17.8 ·10-6 per oC (20-100 C) |
Density | 0.316 lb/in3 at 68 F | 8.75 gm/cm3 @ 20 C |
Electrical Conductivity | 12 %ACS @ 68 F | 0.07 MegaSiemens/cm @ 20 C |
Electrical Resistivity | 86.4 ohms-cmil/ft @ 68 F | 14.36 microhm-cm @ 20 C |
Melting Point - Liquidus | 1940 F | 1060 C |
Melting Point - Solidus | 1890 F | 1032 C |
Modulas of Elasticity in Tension | 17000 ksi | 117000 MPa |
Modulus of Rigidity | 6400 ksi | 44130 MPa |
Specific Gravity | 8.75 | 8.75 |
Specific Heat Capacity | 0.09 Btu/lb/oF at 68 F | 377.1 J/kg · oK at 293 K |
Thermal Conductivity | 33.0 Btu · ft2·oF)at 68F | 57.1 W/m · oK at 20 C |
Sizes Available | |
ROUND RODS/BARS | 8mm To 70 mm |
HEX | 10mm To 60mm |
SQUARE | 10mm To 60mm |
FLAT | 10mm Min Thickness and max Width 120mm |
BILLETS | Up to 200 mm |
INGOTS | As per Specification |
![]() |