C67400 MANGANESE BRONZE

480 INR/Kilograms

Get a Price/Quote

Product Details:

Click to View more

Request to Call Back Send Inquiry

Product Details
Product Description

C67400 MANGANESE BRONZE Price And Quantity

Minimum Order Quantity 250 Kilograms
Price 480 INR/Kilograms
Price Range 450.00 - 500.00 INR/Kilograms

C67400 MANGANESE BRONZE Trade Information

Supply Ability 20000 Kilograms Per Month
Delivery Time 4 Week

Product Description

C67400 MANGANESE BRONZE

EQUIVALENT SPECIFICATIONS

Specifications	Designation
Uns	C66800
Uns	C67300
Uns	C67420

C67400 : Excellent hot and cold workability; good forge ability. Fabricated by bending, coining, coppersmith, drawing and upsetting, hot forging and pressing, knurling, roll threading, shearing, spinning, swaging, and stamping.

INDUSTRIAL: Bushings, Shafts, Cams, Chain Guides, Wear Plates, Gears, Food Conveyor Chain
OTHER: Connecting Rods

Sizes Available :

ROUND RODS. . . . . . . . . . . . . 8mm To 70 mm
HEX . . . . . . . . . . . . . . . 10mm To 60mm
SQUARE . . . . . . 10mm To 60mm
FLAT . . . . . . . . . . .10mm Min Thickness and max Width 120mm
BILLETS. . . . . . . . Up to 200 mm
INGOTS. . . . . . . As per Specification

CHEMICAL COMPOSITION

	Al	Cu	Fe	Pb	Mn	Ni	Si	Sn	Zn
Min/Max	0.50 - 2.0	57.0 - 60.0	0.35	0.5	2.0 - 3.5	0.25	0.50 - 1.5	0.3	Rem
Nominals	1.2000	58.5000	-	-	2.8000	-	1.0000	-	36.5000

SPECIFICATIONS

End Product	Specification
Bar	SAE J461, J463
Forgings	SAE J461, J463
Rod	SAE J463, J461
Shapes	SAE J463, J461

FABRICATION

Joining Technique	Suitability
Brazing	Good
Butt Weld	Good
Capacity for Being Cold Worked	Poor
Capacity for Being Hot Formed	Excellent
Coated Metal Arc Welding	Not Recommended
Forgeability	100
Gas Shielded Arc Welding	Fair
Machinability Rating	30
Oxyacetylene Welding	Not Recommended
Seam Weld	Good
Soldering	Fair
Spot Weld	Good

PHYSICAL PROPERTIES

Product Property	US Customary	Metric
Coefficient of Thermal Expansion	11.0 ·10-6 per oF (68-572 F)	19.8 10-6 per oC (20-300 C)
Density	0.292 lb/in3 at 68 F	8.08 gm/cm3 @ 20 C
Electrical Conductivity	23 %IACS @ 68 F	0.135 MegaSiemens/cm @ 20 C
Electrical Resistivity	45.1 ohms-cmil/ft @ 68 F	7.5 microhm-cm @ 20 C
Melting Point - Liquidus	1625 F	885 C
Melting Point - Solidus	1590 F	866 C
Modulas of Elasticity in Tension	16000 ksi	110000 MPa
Modulus of Rigidity	6000 ksi	41370 MPa
Specific Gravity	8.08	8.08
Specific Heat Capacity	0.09 Btu/lb/oF at 68 F	377.1 J/kg/ · oK at 293 K
Thermal Conductivity	58.0 Btu · ft/(hr · ft2·oF)at 68F	100.4 W/m · oK at 20 C