C35200 Dezincification Resistant Brass
Alloy C352 Brass is a copper-zinc-lead alloy with small proportions of arsenic, mainly having alpha phase structure in the used heat treated condition, with fine dispersion of lead particles. The alloy possess excellent machining ability, good cold forming properties with high resistance to dezincification.
Applications :
Valves, Stopcocks, Taps and Plumbing fittings that comes directly in contact with chlorinated water supplies
Equivelent Specifications: | |
Specifications | Designation |
UNS | C353330 |
BS | CZ 132 |
Europen | CW602N |
Chemical Composition: | ||||
| Cu | As | Pb | Zn |
Min/Max | 61.0 - 63.0 | 0.02-0.15 | 1.7 2.8 | Rem |
Nominals | - | - | - | - |
Fabrication: | |
Hot Working | Poor |
Cold Working | Excellent |
Thread Rolling | Excellent |
Hot Working range | 700 C 800 C |
Melting range | 875 C 890 C |
Mechanical Properties: | |
Product Property | US Customary |
0.2% Proof Stress MPa | 120-200 |
Tensile Strength MPa | 280-450 |
Elongation | 20-40 |
Hardness HV | 80-140 |
Sizes Available: | |
Hollow Rods | Min Bore Size 20 mm and Max OD 100 mm |
Round Rods | 6mm To 130 mm |
Hex | 5mm To 60mm |
Square | 4mm To 60mm |
Flat | 5mm Min Thickness and max Width 120mm |
Profiles / Sections | AS per Customer Drawing |
Billets | Up to 200 mm |
Ingots | AS per Specification |